6061 Aluminum Wires

6061 Aluminum WireSpecifications

Diameter: 0.5mm-15mm

Length: Roll

Alloy Temper: HO,H12,H14,H16,H18,H19,H22,H24,H26,H28,F,H112,T651,T3,T451, T4,T6, ect.

Craft: Cutting, hemming, arc bending, welding, grinding, spraying, forming

Surface: Mill finish, no stains, without rough selvage, Anodizing

Certificate: ISO9001, CE, SGS, etc

Delivery Time: 7-20 days.

6061 Aluminum Wire Data Sheet

Chemical Composition of 6061 Aluminum Wire

Elements	Mg	Fe	Cu	Mn	Si	Cr	Ti	Zn	Others	Al
Content	0.8-1.2	0.70	0.15-0.40	0.15	0.40-0.8	0.04-0.35	0.15	0.25	0.05	Remains

Mechanical Properties and Tempers of 6061 Aluminium Wire

Typical Mechanical Properties of 6061 Aluminium Wire
Temper	Tensile Strength	Yield Strength	Elongation
	KSI	KSI	%
T451	35	21	25
T651	45	40	17

Different Tempers of 6061 Aluminum Wires Metal

6061 aluminum alloy is a commonly used aluminum alloy that can be used to manufacture a variety of products, including sheet metal products. It can be processed in different states to obtain different mechanical properties and uses. The following are several common states of 6061 aluminum wire metal:

T6: This is one of the most common states in 6061 aluminum wire metal. In the T6 state, the aluminum alloy undergoes high-temperature solution treatment and then is rapidly quenched. This process gives it high strength and hardness. 6061 aluminum in T6 temper is commonly used in structural applications where strength is critical.

T4: In this state, the aluminum alloy has been solid solution treated and then aged naturally. It offers good formability and weldability while still possessing reasonable strength. 6061 aluminum in T4 temper is typically used in applications that require forming or bending.

T651 : Similar to the T6 condition, but with additional stretching after solution treatment. This stretching process reduces internal stress and enhances dimensional stability. 6061 aluminum in T651 condition is typically used in applications requiring precision parts and components where tight tolerances are required.

O : This is the annealed state of 6061 aluminum, completely softened. It has excellent formability but is less strong than in the processed state. 6061 aluminum in the O temper is suitable for applications where extensive forming is required or where strength is not a primary consideration.

T6511: This is a stretched version of the T651 condition, achieved through a stretching process. It offers properties similar to T651 aluminum, but with improved flatness and straightness. 6061 aluminum in the T6511 temper is typically used in applications where flatness is critical, such as aerospace components.

These are some of the most common states of 6061 aluminum wires, but there are others available, each offering specific properties suitable for different applications.