6082 Aluminum Bars

6082 Aluminum Bars Specifications

Standards: ASTM B221, B211, B565, B316 3003, DIN AlMnCu

Aluminum bar form: Aluminum round, hexagonal, flat, semi-circular, oval, rectangular black, and glossy finish

Aluminum round bar diameter: 0.1-600mm, etc.

Aluminum hexagonal bar: 0.1-600mm, etc.

Aluminum angle bar size: 0.5mm*40mm*40mm-20mm*400mm*400mm

Aluminum flat steel thickness: 0.1-600mm, etc.

Aluminum flat bar size: 1-2500mm, etc.

Aluminum round bar length: 1-12m, random, fixed, and cut length or according to customer requirements

Product Introduction

Excellent weldability, corrosion resistance, formability and machinability

6082 is a heat treated reinforcable alloy, with good formability, weldability, machinability and corrosion resistance, while having medium strength, can still maintain good operability after annealing, mainly used in mechanical structure, including rods, plates, pipes and profiles. This alloy has similar but not identical mechanical properties to alloy 6061, and its -T6 state has high mechanical properties. Alloy 6082 is a very commonly used alloy product in Europe, and also has a high application in the United States, suitable for processing raw materials, seamless aluminum tubes, structural profiles and custom profiles. Alloy 6082 generally has good processing characteristics and good anode reaction properties. The most commonly used anode reaction methods include removing impurities and staining, coating, etc.

Alloy 6082 combines excellent weldability, brazability, corrosion resistance, formability and machinability. The -0 and T4 states of alloy 6082 are suitable for bending and forming occasions, and its -T5 and -T6 states are suitable for the requirements of good machinability, and some specific processes require the use of chip separators or other special processes to help separate chips; Alloy 6082 generally has good processing characteristics and good anode reaction properties.

Typical uses

The 6082 is widely used in aviation fixtures, trucks, towers, boats, pipes and other applications in buildings that require strength, weldability and corrosion resistance. Such as: aircraft parts, camera lenses, couplers, marine accessories and hardware, electronic accessories and joints, decorative or various hardware, hinge heads, magnetic heads, brake pistons, hydraulic pistons, electrical accessories, valves and valve parts.

Chemical composition

Alloy grade			Si	Fe	Cu	Mn	Mg	Cr	Zn	Ti	Zr	other		AL
New grade	Old grade		0.7-1.3	0.50	0.10	0.4-1.0	0.6-1.2	0.25	0.20	0.10	——	each	total
6082		——										0.05	0.15	Allowance

Mechanical properties

Aluminum alloy grade and state	Tensile strength Rm/Mpa	Yield strength Rp0.2/Mpa	Elongation/%	Hardness/ HBWα
6082-T6	310	260	6	90

Physical properties

Aluminum alloy grade and state	Coefficient of thermal expansion (20-100℃) μm/m·k	Melting point range (℃)	Electrical conductivity 20℃(68℉) (%IACS)	Resistivity20℃(68℉) Ωmm2/m	Density (20℃)(g/cm3)
6082-T6	23.5	621-654	57	0.0302	2.8

Quality characteristics

Density: 2.85g/cm³.

Hardness: O state: 40HB; T4, T451 status: 58HB; T6, T651 Status: 90HB; The data is taken from the 10 mm diameter ball and the test results of 30 s under a load of 500 kg.