2011 aluminum wire is known for its excellent cutting performance and mechanical strength, making it an ideal material for precision parts processing. As a leading metal supplier, HXM provides high-quality 2011 aluminum wire to meet various industrial and commercial needs.
Contact us now to learn more about the performance, applications, and prices of 2011 aluminum wire!
2011 Aluminum Wire Specifications
Diameter: 0.5mm-50mm
Length: Roll
Alloy Temper: O, H12, H14, H16, H18, F, H112,T651,T3,T451, T4,T6, ect.
Craft: Cutting, hemming, arc bending, welding, grinding, spraying, forming
Surface: Mill finish, no stains, without rough selvage, Anodizing
Certificate: ISO9001, CE, SGS, etc
Delivery Time: 7-20 days.
Standard: ASTM B211、EN AW-2011, etc.
2011 Aluminum Wire Data Sheet
Equivalent Specifications of Aluminium 2011 Wires
here’s a table displaying the equivalent specifications of the Aluminum 2011 Wires
| Specification | Standard/Organization | Details |
|---|---|---|
| EN | EN AW-2011 | European Norm equivalent for 2011 aluminum alloy |
| ASTM | ASTM B209 | Standard Specification for Aluminum and Aluminum-Alloy Sheet and Plate |
| UNS | UNS A92011 | Unified Numbering System designation for 2011 aluminum |
| AA | AA2011 | Aluminum Association designation for 2011 alloy |
| ISO | ISO 6361 | International Organization for Standardization – Wrought aluminum and aluminum alloy sheets, strips, and plates |
| DIN | DIN 3.1655 | Deutsches Institut für Normung (German Institute for Standardization) equivalent for 2011 aluminum |
| JIS | JIS H 4000 | Japanese Industrial Standards for aluminum and aluminum alloys |
| GB | GB/T 3190 | National Standard of the People’s Republic of China for aluminum and aluminum alloy chemical composition |
| AMS | AMS 4027 | Aerospace Material Specification for 2011 aluminum alloy sheets and plates |
| SAE | SAE J454 | Society of Automotive Engineers – Wrought aluminum and aluminum alloy sheets and plates |
This table outlines the various standards and specifications that are equivalent to Aluminum 2011 Wires. If you would like more information, please contact us directly!
Chemical Composition of 2011 Aluminum Wires
Here is the chemical composition of the 2011 Aluminum Wires:
| Element | Composition (%) |
|---|---|
| Al | Balance |
| Cu | 5.0 – 6.0 |
| Fe | ≤ 0.7 |
| Si | ≤ 0.4 |
| Zn | ≤ 0.3 |
| Pb | 0.2 – 0.6 |
| Bi | 0.2 – 0.6 |
| Others | Each ≤ 0.05%, Total ≤ 0.15 |
This is the specific percentage range of various elements of the 2011 aluminum wires, which ensures its unique properties and performance characteristics. If you want to know more, please contact us directly!
Mechanical Properties of 2011 Aluminium Wires
| Property | Value |
|---|---|
| Ultimate Tensile Strength | 310 MPa (45 ksi) |
| Yield Strength | 276 MPa (40 ksi) |
| Elongation | Approximately 10% in 2 inches |
| Hardness | 95 HB |
| Modulus of Elasticity | 69 GPa (10,000 ksi) |
| Shear Strength | 207 MPa (30 ksi) |
The mechanical properties demonstrated above make the 2011 aluminum wires an excellent choice for applications that require high strength and precision machining. Its excellent machinability and ability to achieve a high-quality surface finish ensure its optimal performance in a variety of industrial uses.
For more information on the 2011 aluminum wires or to request a quote, please contact HXM. Our sales team will respond to you within 24 hours!
Physical Properties of 2011 Aluminum Wires
| Property | Value |
|---|---|
| Density | 2.85 g/cm³ (0.103 lb/in³) |
| Melting Point | 502 – 638°C (936 – 1180°F) |
| Thermal Conductivity | 121 W/m·K |
| Electrical Conductivity | 32% IACS |
| Coefficient of Thermal Expansion | 23.6 x 10⁻⁶ /°C (13.1 x 10⁻⁶ /°F) |
| Specific Heat Capacity | 0.87 J/g-°C |
These physical properties highlight the excellent thermal and electrical conductivity of the 2011 aluminum wires, as well as its suitability for high-temperature applications due to its melting point range and thermal expansion coefficient. Specific heat capacity and density further highlight the efficiency and reliability of this material.
For more details on 2011 aluminum wires, please contact HXM, our team will respond to you within 24 hours!
Tempers of 2011 Aluminum Wires
| Temper Designation | Description | Typical Applications |
|---|---|---|
| 2011-T3 | Solution heat-treated, cold-worked, and naturally aged. | Suitable for applications requiring high strength and good machinability. |
| 2011-T4 | Solution heat-treated and naturally aged. | General-purpose applications with a good balance of strength and ductility. |
| 2011-T6 | Solution heat-treated and artificially aged. | Offers the highest strength and is used in critical components where high performance is required. |
| 2011-T8 | Solution heat-treated, cold-worked, and artificially aged. | Provides excellent machinability and good strength, often used in complex, precision machined parts. |
| 2011-O | Annealed (softened). | Ideal for applications requiring maximum ductility and formability. |
These tempering treatments allow 2011 aluminum wires to be customized to specific application requirements, ensuring optimal performance in a variety of industrial and engineering environments.
For more information or pricing on 2011 aluminum wires, please contact HXM and our team will respond to your message within 24 hours!
Applications of 2011 Aluminum Wire Metal
2011 Aluminum Wire Packages
The following is our company’s standard aluminum wire export packaging. If the customer has any packaging requirements, our company can meet them.